Surface adhesion of pMDI resin on wood biopolymer model films

verfasst von: Eko Setio Wibowo, Byung-Dae Park

Erschienen in: European Journal of Wood and Wood Products | Ausgabe 5/2023

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Even though polymeric diphenylmethane diisocyanate (pMDI) resin shows strong adhesion in wood bonding, its adhesion to major wood biopolymers is not fully understood. Thus, this study reports the surface adhesion of pMDI resin on wood biopolymer model films, such as cellulose, hemicellulose and lignin. The effects of wood biopolymer chemical structure, surface roughness, and wettability on the adhesion measurement were examined. The results revealed that, in general, pMDI exhibited greater adhesive force toward lignin model films compared with other biopolymer films. This is because lignin has abundant phenolic hydroxyl groups and aromatic rings, smoother surface, and higher surface-free energy than celluloses and hemicelluloses. This result suggests that the surface properties and hydroxyl group content of wood biopolymer provide a significant role in the bonding interaction between pMDI resin and wood biopolymers.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
Zurück zum Zitat Abranches DO, Martins MAR, Silva LP et al (2019) Phenolic hydrogen bond donors in the formation of non-ionic deep eutectic solvents: the quest for type v des. Chem Commun 55:10253–10256CrossRef Abranches DO, Martins MAR, Silva LP et al (2019) Phenolic hydrogen bond donors in the formation of non-ionic deep eutectic solvents: the quest for type v des. Chem Commun 55:10253–10256CrossRef
Zurück zum Zitat Dos Santos DM, De Lacerda Bukzem A, Ascheri DPR et al (2015) Microwave-assisted carboxymethylation of cellulose extracted from brewer’s spent grain. Carbohydr Polym 131:125–133CrossRefPubMed Dos Santos DM, De Lacerda Bukzem A, Ascheri DPR et al (2015) Microwave-assisted carboxymethylation of cellulose extracted from brewer’s spent grain. Carbohydr Polym 131:125–133CrossRefPubMed
Zurück zum Zitat Fodil Cherif M, Trache D, Brosse N et al (2020) Comparison of the physicochemical properties and thermal stability of organosolv and Kraft Lignins from Hardwood and softwood biomass for their potential valorization. Waste Biomass Valoriz 11:6541–6553CrossRef Fodil Cherif M, Trache D, Brosse N et al (2020) Comparison of the physicochemical properties and thermal stability of organosolv and Kraft Lignins from Hardwood and softwood biomass for their potential valorization. Waste Biomass Valoriz 11:6541–6553CrossRef
Zurück zum Zitat Gustafsson E, Johansson E, Wågberg L, Pettersson T (2012) Direct adhesive measurements between Wood Biopolymer Model Surfaces. Biomacromolecules 13:3046–3053CrossRefPubMed Gustafsson E, Johansson E, Wågberg L, Pettersson T (2012) Direct adhesive measurements between Wood Biopolymer Model Surfaces. Biomacromolecules 13:3046–3053CrossRefPubMed
Zurück zum Zitat He G, Yan N (2005) Effect of moisture content on curing kinetics of pMDI resin and wood mixtures. Int J Adhes Adhes 25:450–455CrossRef He G, Yan N (2005) Effect of moisture content on curing kinetics of pMDI resin and wood mixtures. Int J Adhes Adhes 25:450–455CrossRef
Zurück zum Zitat He G, Yan N (2007) Curing kinetics of polymeric diphenylmethane diisocyanate with different wood species. Int J Adhes Adhes 27:244–249CrossRef He G, Yan N (2007) Curing kinetics of polymeric diphenylmethane diisocyanate with different wood species. Int J Adhes Adhes 27:244–249CrossRef
Zurück zum Zitat Kacuráková M, Capek P, Sasinková V et al (2000) FT-IR study of plant cell wall model compounds: pectic polysaccharides and hemicelluloses. Carbohydr Polym 43:195–203CrossRef Kacuráková M, Capek P, Sasinková V et al (2000) FT-IR study of plant cell wall model compounds: pectic polysaccharides and hemicelluloses. Carbohydr Polym 43:195–203CrossRef
Zurück zum Zitat Lemmerer A, Esterhuysen C (2011) OHphenol⋯OHalcohol hydrogen-bonding as the preferred hydrogen-bonded interaction in the crystal structures of three isomers of methylolphenol: analysis of hydrogen-bonding interactions in phenol and alcohol containing molecules. CrystEngComm 13:5773–5782CrossRef Lemmerer A, Esterhuysen C (2011) OHphenol⋯OHalcohol hydrogen-bonding as the preferred hydrogen-bonded interaction in the crystal structures of three isomers of methylolphenol: analysis of hydrogen-bonding interactions in phenol and alcohol containing molecules. CrystEngComm 13:5773–5782CrossRef
Zurück zum Zitat Li H, McDonald AG (2014) Fractionation and characterization of industrial lignins. Ind Crops Prod 62:67–76CrossRef Li H, McDonald AG (2014) Fractionation and characterization of industrial lignins. Ind Crops Prod 62:67–76CrossRef
Zurück zum Zitat Lubis MAR, Park BD, Lee SM (2019) Performance of hybrid adhesives of blocked-pMDI/melamine-urea-formaldehyde resins for the surface lamination on plywood. J Korean Wood Sci Technol 47:200–209CrossRef Lubis MAR, Park BD, Lee SM (2019) Performance of hybrid adhesives of blocked-pMDI/melamine-urea-formaldehyde resins for the surface lamination on plywood. J Korean Wood Sci Technol 47:200–209CrossRef
Zurück zum Zitat Mansouri HR, Pizzi A, Leban J-M (2006) Improved water resistance of UF adhesives for plywood by small pMDI additions. Holz Roh- Werkst 64:218–220CrossRef Mansouri HR, Pizzi A, Leban J-M (2006) Improved water resistance of UF adhesives for plywood by small pMDI additions. Holz Roh- Werkst 64:218–220CrossRef
Zurück zum Zitat Melilli G, Carmagnola I, Tonda-Turo C et al (2020) DLP 3D printing meets lignocellulosic biopolymers: Carboxymethyl cellulose inks for 3D biocompatible hydrogels. Polym (Basel) 12:1–11 Melilli G, Carmagnola I, Tonda-Turo C et al (2020) DLP 3D printing meets lignocellulosic biopolymers: Carboxymethyl cellulose inks for 3D biocompatible hydrogels. Polym (Basel) 12:1–11
Zurück zum Zitat Pimenta AS, Trianoski R, Pizzi A et al (2019) Effect of polymeric diisocyanate addition on bonding performance of a demethylated-pyrolysis-oil-based adhesive. Wood Sci Technol 53:1311–1337CrossRef Pimenta AS, Trianoski R, Pizzi A et al (2019) Effect of polymeric diisocyanate addition on bonding performance of a demethylated-pyrolysis-oil-based adhesive. Wood Sci Technol 53:1311–1337CrossRef
Zurück zum Zitat Sharma K, Khaire KC, Thakur A et al (2020) Acacia Xylan as a substitute for commercially available Xylan and its application in the production of Xylooligosaccharides. ACS Omega 5:13729–13738CrossRefPubMedPubMedCentral Sharma K, Khaire KC, Thakur A et al (2020) Acacia Xylan as a substitute for commercially available Xylan and its application in the production of Xylooligosaccharides. ACS Omega 5:13729–13738CrossRefPubMedPubMedCentral
Zurück zum Zitat Simon C, George B, Pizzi A (2002) Copolymerization in UF/pMDI adhesives networks. J Appl Polym Sci 86:3681–3688CrossRef Simon C, George B, Pizzi A (2002) Copolymerization in UF/pMDI adhesives networks. J Appl Polym Sci 86:3681–3688CrossRef
Zurück zum Zitat Solt P, Libowitzky S, van Herwijnen HWG, Konnerth J (2020) Improved method for analyzing cohesive strength development of pMDI. Wood Sci Technol 54:7–17CrossRef Solt P, Libowitzky S, van Herwijnen HWG, Konnerth J (2020) Improved method for analyzing cohesive strength development of pMDI. Wood Sci Technol 54:7–17CrossRef
Zurück zum Zitat Sonnenschein MF, Wendt BL (2005) Efficacy of polymeric MDI/Polyol mixtures for binding wood boards. Wood Sci Technol 39:27–35CrossRef Sonnenschein MF, Wendt BL (2005) Efficacy of polymeric MDI/Polyol mixtures for binding wood boards. Wood Sci Technol 39:27–35CrossRef
Zurück zum Zitat Stöckel F, Konnerth J, Moser J et al (2012) Micromechanical properties of the interphase in pMDI and UF bond lines. Wood Sci Technol 46:611–620CrossRef Stöckel F, Konnerth J, Moser J et al (2012) Micromechanical properties of the interphase in pMDI and UF bond lines. Wood Sci Technol 46:611–620CrossRef
Zurück zum Zitat Synytsya A, Čopíková J, Matějka P, Machovič V (2003) Fourier transform Raman and infrared spectroscopy of pectins. Carbohydr Polym 54:97–106CrossRef Synytsya A, Čopíková J, Matějka P, Machovič V (2003) Fourier transform Raman and infrared spectroscopy of pectins. Carbohydr Polym 54:97–106CrossRef
Zurück zum Zitat Wang X, Zhao L, Deng Y et al (2018) Effect of the penetration of isocyanates (pMDI) on the nanomechanics of wood cell wall evaluated by AFM-IR and nanoindentation (NI). Holzforschung 72:301–309CrossRef Wang X, Zhao L, Deng Y et al (2018) Effect of the penetration of isocyanates (pMDI) on the nanomechanics of wood cell wall evaluated by AFM-IR and nanoindentation (NI). Holzforschung 72:301–309CrossRef
Zurück zum Zitat Weaver FW, Owen NL (1995) Isocyanate-wood adhesive bond. Appl Spectrosc 49:171–176CrossRef Weaver FW, Owen NL (1995) Isocyanate-wood adhesive bond. Appl Spectrosc 49:171–176CrossRef
Zurück zum Zitat Wendler SL, Frazier CE (1996) Effect of moisture content on the isocyanate/wood adhesive bondline by15N CP/MAS NMR. J Appl Polym Sci 61:775–782CrossRef Wendler SL, Frazier CE (1996) Effect of moisture content on the isocyanate/wood adhesive bondline by15N CP/MAS NMR. J Appl Polym Sci 61:775–782CrossRef
Zurück zum Zitat Wibowo ES, Park B-D (2021) Direct measurement of surface adhesion between thin films of nanocellulose and urea–formaldehyde resin adhesives. Cellulose 28:8459–8481CrossRef Wibowo ES, Park B-D (2021) Direct measurement of surface adhesion between thin films of nanocellulose and urea–formaldehyde resin adhesives. Cellulose 28:8459–8481CrossRef
Zurück zum Zitat Wibowo ES, Park B-D (2022a) Effect of hemicellulose molecular structure on wettability and surface adhesion to urea–formaldehyde resin adhesives. Wood Sci Technol 56:1047–1070CrossRef Wibowo ES, Park B-D (2022a) Effect of hemicellulose molecular structure on wettability and surface adhesion to urea–formaldehyde resin adhesives. Wood Sci Technol 56:1047–1070CrossRef
Zurück zum Zitat Wibowo ES, Park B (2022b) The role of acetone-fractionated Kraft lignin molecular structure on surface adhesion to formaldehyde-based resins. Int J Biol Macromol 225:1449–1461CrossRefPubMed Wibowo ES, Park B (2022b) The role of acetone-fractionated Kraft lignin molecular structure on surface adhesion to formaldehyde-based resins. Int J Biol Macromol 225:1449–1461CrossRefPubMed
Zurück zum Zitat Wu T, Kummer N, De France KJ et al (2021) Nanocellulose–lysozyme colloidal gels via electrostatic complexation. Carbohydr Polym 251:1–9CrossRef Wu T, Kummer N, De France KJ et al (2021) Nanocellulose–lysozyme colloidal gels via electrostatic complexation. Carbohydr Polym 251:1–9CrossRef
Zurück zum Zitat Xu G-Z, Eom Y-G, Lee B-H, Kim H-J (2010) Effect of pMDI or HDI content in UMF resin on bonding high moisture content veneers. J Korean Wood Sci Technol 38:414–420CrossRef Xu G-Z, Eom Y-G, Lee B-H, Kim H-J (2010) Effect of pMDI or HDI content in UMF resin on bonding high moisture content veneers. J Korean Wood Sci Technol 38:414–420CrossRef
Zurück zum Zitat Yelle DJ, Ralph J, Frihart CR (2011a) Delineating pMDI model reactions with loblolly pine via solution-state NMR spectroscopy. Part 2. Non-catalyzed reactions with the wood cell wall. Holzforschung 65:145–154 Yelle DJ, Ralph J, Frihart CR (2011a) Delineating pMDI model reactions with loblolly pine via solution-state NMR spectroscopy. Part 2. Non-catalyzed reactions with the wood cell wall. Holzforschung 65:145–154
Zurück zum Zitat Yelle DJ, Ralph J, Frihart CR (2011b) Delineating pMDI model reactions with loblolly pine via solution-state NMR spectroscopy. Part 1. Catalyzed reactions with wood models and wood polymers. Holzforschung 65:131–143 Yelle DJ, Ralph J, Frihart CR (2011b) Delineating pMDI model reactions with loblolly pine via solution-state NMR spectroscopy. Part 1. Catalyzed reactions with wood models and wood polymers. Holzforschung 65:131–143
Zurück zum Zitat Zhou X, Frazier CE (2001) Double labeled isocyanate resins for the solid-state NMR detection of urethane linkages to wood. Int J Adh Adhes 21(3):259–264CrossRef Zhou X, Frazier CE (2001) Double labeled isocyanate resins for the solid-state NMR detection of urethane linkages to wood. Int J Adh Adhes 21(3):259–264CrossRef
Metadaten
Titel
Surface adhesion of pMDI resin on wood biopolymer model films
verfasst von
Eko Setio Wibowo
Byung-Dae Park
Publikationsdatum
27.04.2023
Verlag
Springer Berlin Heidelberg
Erschienen in
European Journal of Wood and Wood Products / Ausgabe 5/2023
Print ISSN: 0018-3768
Elektronische ISSN: 1436-736X
DOI
https://doi.org/10.1007/s00107-023-01958-z

Weitere Artikel der Ausgabe 5/2023

European Journal of Wood and Wood Products 5/2023 Zur Ausgabe