Physics of Metals and Metallography

Erschienen in:

29.12.2023 | STRENGTH AND PLASTICITY

Effect of Cold-Drawing Deformation on the Microstructure and Properties of AA2024-T8

verfasst von: Y. X. Jia, R. M. Su, W. J. Zhang, G. L. Li, Y. D. Qu, R. D. Li

Erschienen in: Physics of Metals and Metallography | Ausgabe 13/2023

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

T8 treatment includes solution treatment, cold working and artificial aging treatment. T8 treatment can greatly improve the hardness and strength of 2024 aluminum alloy without reducing the corrosion resistance. The effect of 0, 1, 2, 3, and 4% cold-drawing deformation on the microstructures of the alloy was observed by transmission electron microscopy, and properties of the alloy was investigated by hardness tests, tensile tests and electrochemical corrosion tests. The results show that the mechanical properties and corrosion resistance of cold-drawing deformed 2024 aluminum alloy are better than those of non-deformed alloy. Compared with AA2024-T6, AA2024-T8 with 2% cold-drawing deformation has a higher hardness by 11.3%, and a higher tensile strength by 10.8%. The improvement of the properties of AA2024-T8 is mainly due to the interaction between dislocations and precipitates. With the increase in cold-drawing deformation, the nucleation points of precipitates in AA2024-T8 gradually increase, and precipitates are gradually coarsened under the same artificial aging treatment.

Vorheriger Artikel Study on Nucleation and Growth of Columnar Grains in Non-Oriented Steel by Phase Transformation

Nächster Artikel Strengthening Mechanisms of Rails’ Surface in Ultra Long-Term Operation

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 340 Zeitschriften

aus folgenden Fachgebieten:

Bauwesen + Immobilien
Business IT + Informatik
Finance + Banking
Management + Führung
Marketing + Vertrieb
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

C. Fan, L. Ou, Z. Hu, J. Yang, and X. Chen, “Re-dissolution and re-precipitation behavior of nano-precipitated phase in Al−Cu−Mg alloy subjected to rapid cold stamping,” Trans. Nonferrous Met. Soc. China 29, 2455–2462 (2019). https://doi.org/10.1016/s1003-6326(19)65153-8CrossRef

Y. Liu, F. Teng, F. H. Cao, Z. X. Yin, Y. Jiang, S. B. Wang, and P. K. Shen, “Defective GP-zones and their evolution in an Al–Cu–Mg alloy during high-temperature aging,” J. Alloys Compd. 774, 988–996 (2019). https://doi.org/10.1016/j.jallcom.2018.10.061CrossRef

M. H. Ghoncheh, S. G. Shabestari, A. Asgari, and M. Karimzadeh, “Nonmechanical criteria proposed for prediction of hot tearing sensitivity in 2024 aluminum alloy,” Trans. Nonferrous Met. Soc. China 28, 848–857 (2018). https://doi.org/10.1016/s1003-6326(18)64718-1CrossRef

M.-L. De Bonfils-Lahovary, L. Laffont, and C. Blanc, “Characterization of intergranular corrosion defects in a 2024 T351 aluminium alloy,” Corros. Sci. 119, 60–67 (2017). https://doi.org/10.1016/j.corsci.2017.02.020CrossRef

F. M. Queiroz, M. Terada, A. F. S. Bugarin, H. G. De Melo, and I. Costa, “Comparison of corrosion resistance of the AA2524-T3 and the AA2024-T3,” Metals 11, 980 (2021). https://doi.org/10.3390/met11060980CrossRef

F. Z. Lemmadi, A. Chala, O. Belahssen, and S. Benramache, “Effect of heat treatments on structural, microstructural and mechanical properties of Al 2017 alloy,” Phys. Met. Metallogr. 117, 83–88 (2016). https://doi.org/10.1134/s0031918x16010099ADSCrossRef

C. Rockenhäuser, C. Rowolt, B. Milkereit, R. Darvishi Kamachali, O. Kessler, and B. Skrotzki, “On the long-term aging of S-phase in aluminum alloy 2618A,” J. Mater. Sci. 56, 8704–8716 (2021). https://doi.org/10.1007/s10853-020-05740-xADSCrossRef

S. Sun, Yi. Fang, L. Zhang, C. Li, and S. Hu, “Effects of aging treatment and peripheral coarse grain on the exfoliation corrosion behaviour of 2024 aluminium alloy using SR-CT,” J. Mater. Res. Technol. 9, 3219–3229 (2020). https://doi.org/10.1016/j.jmrt.2020.01.069CrossRef

W. Shi, H. Zhou, and X. Zhang, “High-strength and anti-corrosion of Al–Cu–Mg alloy by controlled ageing process,” Philos. Mag. Lett. 99, 235–242 (2019). https://doi.org/10.1080/09500839.2019.1662960ADSCrossRef

10.

Y. C. Lin, G. Liu, M.-S. Chen, J.-L. Zhang, Zh.-G. Chen, Yu-Q. Jiang, and J. Li, “Corrosion resistance of a two-stage stress-aged Al–Cu–Mg alloy: Effects of external stress,” J. Alloys Compd. 661, 221–230 (2016). https://doi.org/10.1016/j.jallcom.2015.11.173CrossRef

11.

H. He, Yo. Yi, S. Huang, W. Guo, and Yu. Zhang, “Effects of thermomechanical treatment on grain refinement, second-phase particle dissolution, and mechanical properties of 2219 Al alloy,” J. Mater. Process. Technol. 278, 116506 (2020). https://doi.org/10.1016/j.jmatprotec.2019.116506CrossRef

12.

H. Li, W. Xu, Z. Wang, B. Fang, R. Song, and Z. Zheng, “Effects of re-ageing treatment on microstructure and tensile properties of solution treated and cold-rolled Al–Cu–Mg alloys,” Mater. Sci. Eng., A 650, 254–263 (2016). https://doi.org/10.1016/j.msea.2015.10.051CrossRef

13.

Y. J. Huang, Z. G. Chen, and Z. Q. Zheng, “A conventional thermo-mechanical process of Al–Cu–Mg alloy for increasing ductility while maintaining high strength,” Scr. Mater. 64, 382–385 (2011). https://doi.org/10.1016/j.scriptamat.2010.10.037CrossRef

14.

X.-Ya. Liu, Zh.-P. Wang, Q.-Sh. Li, X.-L. Zhang, H.‑X. Cui, and X.-L. Zhang, “Effects of pre-deformation on microstructure and properties of Al–Cu–Mg–Ag heat-resistant alloy,” J. Cent. S. Univ. 24, 1027–1033 (2017). https://doi.org/10.1007/s11771-017-3505-xCrossRef

15.

H. Wang, Yo. Yi, and S. Huang, “Influence of pre-deformation and subsequent ageing on the hardening behavior and microstructure of 2219 aluminum alloy forgings,” J. Alloys Compd. 685, 941–948 (2016). https://doi.org/10.1016/j.jallcom.2016.06.111CrossRef

16.

X. Li, K. Lei, P. Song, X. Liu, F. Zhang, J. Li, and J. Chen, “Strengthening of aluminum alloy 2219 by thermo-mechanical treatment,” J. Mater. Eng. Perform. 24, 3905–3911 (2015). https://doi.org/10.1007/s11665-015-1665-0CrossRef

17.

T. S. Parel, S. C. Wang, and M. J. Starink, “Hardening of an Al–Cu–Mg alloy containing Types I and II S phase precipitates,” Mater. Des. 31, S2–S5 (2010). https://doi.org/10.1016/j.matdes.2009.12.048CrossRef

18.

A. Balbo, A. Frignani, V. Grassi, and F. Zucchi, “Electrochemical behaviour of AA2198 and AA2139 in neutral solutions,” Mater. Corros. 66, 796–802 (2015). https://doi.org/10.1002/maco.201408059CrossRef

19.

L. Huang, K. Chen, and S. Li, “Influence of grain-boundary pre-precipitation and corrosion characteristics of inter-granular phases on corrosion behaviors of an Al–Zn–Mg–Cu alloy,” Mater. Sci. Eng., B 177, 862–868 (2012). https://doi.org/10.1016/j.mseb.2012.04.008CrossRef

20.

K. S. Ghosh and K. Tripati, “Microstructural characterization and electrochemical behavior of AA2014 Al-Cu–Mg–Si alloy of various tempers,” J. Mater. Eng. Perform. 27, 5926–5937 (2018). https://doi.org/10.1007/s11665-018-3694-yCrossRef

21.

U. Donatus, R. M. da Silva, J. V. de Sousa Araujo, M. X. Milagre, C. P. de Abreu, C. de Souza Carvalho Machado, and I. Costa, “Macro and microgalvanic interactions in friction stir weldment of AA2198-T851 alloy,” J. Mater. Res. Technol. 8, 6209–6222 (2019). https://doi.org/10.1016/j.jmrt.2019.10.015CrossRef

22.

S. Chen, K. Chen, G. Peng, L. Jia, and P. Dong, “Effect of heat treatment on strength, exfoliation corrosion and electrochemical behavior of 7085 aluminum alloy,” Mater. Des. 35, 93–98 (2012). https://doi.org/10.1016/j.matdes.2011.09.033CrossRef

23.

L. Wen, Ya. Wang, Yu. Zhou, J. Ouyang, L. Guo, and D. Jia, “Corrosion evaluation of microarc oxidation coatings formed on 2024 aluminium alloy,” Corros. Sci. 52, 2687–2696 (2010). https://doi.org/10.1016/j.corsci.2010.04.022CrossRef

24.

K. Wang, R. Su, T. Liu, Yi. Qu, and R. Li, “Electrochemical assessment of laser heat treatment of an Al–Zn–Mg–Cu alloy,” Mater. Corros. 71, 374–381 (2020). https://doi.org/10.1002/maco.201911154CrossRef

25.

S. Wang and M. Starink, “Precipitates and intermetallic phases in precipitation hardening Al–Cu–Mg–(Li) based alloys,” Int. Mater. Rev. 50, 193–215 (2005). https://doi.org/10.1179/174328005x14357CrossRef

26.

H.-Zh. Li, R.-M. Liu, X.-P. Liang, M. Deng, H.-J. Liao, and L. Huang, “Effect of pre-deformation on microstructures and mechanical properties of high purity Al–Cu–Mg alloy,” Trans. Nonferrous Met. Soc. China 26, 1482–1490 (2016). https://doi.org/10.1016/s1003-6326(16)64253-xCrossRef

27.

S. C. Wang and M. J. Starink, “Two types of S phase precipitates in Al–Cu–Mg alloys,” Acta Mater. 55, 933–941 (2007). https://doi.org/10.1016/j.actamat.2006.09.015ADSCrossRef

28.

R. Oltra, B. Vuillemin, F. Rechou, and C. Henon, “Effect of aeration on the microelectrochemical characterization of Al₂Cu intermetallic phases,” Electrochem. Solid-State Lett. 12, C29–C31 (2009). https://doi.org/10.1149/1.3224876CrossRef

29.

M. Araghchi, H. Mansouri, R. Vafaei, and Yi. Guo, “A novel cryogenic treatment for reduction of residual stresses in 2024 aluminum alloy,” Mater. Sci. Eng., A 689, 48–52 (2017). https://doi.org/10.1016/j.msea.2017.01.095CrossRef

30.

R. K. W. Marceau, G. Sha, R. N. Lumley, and S. P. Ringer, “Evolution of solute clustering in Al–Cu–Mg alloys during secondary ageing,” Acta Mater. 58, 1795–1805 (2010). https://doi.org/10.1016/j.actamat.2009.11.021ADSCrossRef

31.

R. K. W. Marceau, G. Sha, R. Ferragut, A. Dupasquier, and S. P. Ringer, “Solute clustering in Al–Cu–Mg alloys during the early stages of elevated temperature ageing,” Acta Mater. 58, 4923–4939 (2010). https://doi.org/10.1016/j.actamat.2010.05.020ADSCrossRef

32.

S. C. Wang, M. J. Starink, and N. Gao, “Precipitation hardening in Al–Cu–Mg alloys revisited,” Scr. Mater. 54, 287–291 (2006). https://doi.org/10.1016/j.scriptamat.2005.09.010CrossRef

33.

M. J. Starink and S. C. Wang, “The thermodynamics of and strengthening due to co-clusters: General theory and application to the case of Al–Cu–Mg alloys,” Acta Mater. 57, 2376–2389 (2009). https://doi.org/10.1016/j.actamat.2009.01.021ADSCrossRef

34.

L. C. Abodi, J. A. DeRose, S. Van Damme, A. Demeter, T. Suter, and J. Deconinck, “Modeling localized aluminum alloy corrosion in chloride solutions under non-equilibrium conditions: Steps toward understanding pitting initiation,” Electrochim. Acta 63, 169–178 (2012). https://doi.org/10.1016/j.electacta.2011.12.074CrossRef

35.

R. Su, S. Ma, K. Wang, G. Li, Yi. Qu, and R. Li, “Effect of cyclic deep cryogenic treatment on corrosion resistance of 7075 alloy,” Met. Mater. Int. 28, 862–870 (2022). https://doi.org/10.1007/s12540-021-00975-yCrossRef

Titel: Effect of Cold-Drawing Deformation on the Microstructure and Properties of AA2024-T8
verfasst von: Y. X. Jia
R. M. Su
W. J. Zhang
G. L. Li
Y. D. Qu
R. D. Li
Publikationsdatum: 29.12.2023
Verlag: Pleiades Publishing
Erschienen in: Physics of Metals and Metallography / Ausgabe 13/2023
Print ISSN: 0031-918X
Elektronische ISSN: 1555-6190
DOI: https://doi.org/10.1134/S0031918X22100362

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Wirtschaft"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 13/2023

Wear Performances of Hypereutectoid P/M Steels Subjected to Different Heat Treatments

Microstructure and Properties of Cu–Ti Alloys Prepared by Aluminothermic Reaction and Subsequent Rolling

Microstructural Evolution and Mechanical Behavior of SP-700Ti Alloy during Superplastic Deformation

Effect of Self-Inoculation Treatment on Microstructure and Mechanical Properties of Eutectic Al–Si Alloy

Precipitation Behavior of Primary Carbide in H13 Bloom Die Steel

Strengthening Mechanisms of Rails’ Surface in Ultra Long-Term Operation